| Property Name |
Polyimide film 6051 |
| Appearance |
Transparent or semi-transparent golden film with smooth and flat surface and without any needle cavities, bubbles or electrically conductive impurities. |
Thickness
Nominal(¦Ìm) |
25.0 |
50.0 |
75.0 |
100.0 |
125.0 |
175.0 |
Thickness
Tolerance(¦Ìm) |
¡À3.0 |
¡À5.0 |
¡À7.5 |
¡À10 |
¡À12.5 |
¡À17.5 |
| Width(mm) |
6¡«660 |
6¡«520 |
| Length (m) |
1000+5 |
500+5 |
300+5 |
200+5 |
| Tensile Strength Mpa ¡Ý |
160 |
120 |
| Elongation at Rupture£¥¡Ý |
50 |
60 |
| Dielectric Strength MV/m ¡Ý |
150 |
120 |
| Surface Resistivity¦¸ ¡Ý |
1.0¡Á1013 |
| Volume Resistivity¦¸.cm ¡Ý |
1.0¡Á1015 |
| Dielectric Constant(106H) |
3¡«4 |
| Dielectric Tangent(106H)¡Ü |
1.0¡Á10-3 |
* All above-mentioned techniques are the average values obtained after our several testing by acknowledged and reliable testing methods.In order to ensure the correct selection and using of our products.please make a thorough understanding both of the purposes and conditions on usage in advance,or notify us so as to provide you with further explanation and service.
Package and Other terms:
Materials of core Hard paper or Plastic
Specification of core£º 76mm(3")
Pakage£º Inside£º Polythene film; Outside£º Carton or Wooden case
Store£º Sealed in dry place, quality guaranteed for two years
1. The film should be provided in rolls and wound up to the pipe core, each roll is well packed and loaded with plastic bag to be placed into dry and clean box.
2. Each box packing should be marked with the type, product specification, size, lot number, gross weight, net weight, date of manufacture, name of the manufacturer and the product acceptances certificate is attached. At the same time the painting words of Dampproof collision-proof ect. Should be marked.
3. The film should be preserved in dry and clean room, the preservation period from the date of production is two years and can still be used when it is qualified in case of the preservation period is exceeded and checked according to standard.
4. During the preservation and transportation, damping and mechanical damage should be avoided.
|